Molykote HSC Plus Paste
Molykote HCS Solid Lubricant Paste
| Product | HCS-Plus Paste |
| Product type | Anti-seize Pastes |
| Technology | Mineral Yağ |
| Solid Lubricants | Copper, MoS2, white solids |
| Quality Class | ISO 9001 |
| Low Temperature | -30°C |
| High Temperature | 1100°C |
| Color | Copper |
| Brand | Molykote |
| Origin | Spain |
Please fill out the form below or call us at +90 312 386 1464 to get in contact with our sales representatives.
General product informationFeatures
- Solid lubricant paste; free of lead or nickel
- Can be used over a wide range of temperatures (-30°C to 1100°C)
- Enables nondestructive dismantling, even after long use at high temperatures
- High load-carrying capacity
- Good corrosion protection
- Good electrical conductivity
- Low speed performance
- Formulated with solid lubricants such as copper, MoS2, white solids
- Used in threaded connections fasteners, chemical-petrochemical plants
- ISO 9001 quality standards
- Brand Molykote, origin Spain
Product technical specificationsTechnical Specifications
MOLYKOTE® HSC Plus Paste
Features
A mineral oil based anti-sieze paste formulated with solid lubricants such as copper, molybdenum disulfide, and white solids.
Applications
For metal/metal combinations that are subjected to high temperatures and frictional contacts that typically for bolted joints, are free from lead or nickel. Suitable for lubrication points with low speeds, subjected to high temperatures and corrosive effects, and also require a low and constant coefficient of friction. As a contact Lubricant for electrically conducting components.Used successfully for stud bolts of gas and steam turbines, stud bolts of turbochargers of diesel engines, flanged connections in chemical and petrochemical plants.
- Electrical
- Threaded connections fasteners
Performance Advantages
- Can be used over a wide range of temperatures (-30°C/-22°F to 1,100°C/2,012°F)
- Enables nondestructive dismantling, even after long use at high temperatures
- High load-carrying capacity
- Due to stated coefficient of friction, defined pre-stressing forces for bolted joints can be achieved
- Good corrosion protection
- Good electrical conductivity
- Low speed performance